Prepregs
Whenever a maximum performance is needed in composite construction, prepregs (pre-impregnated) are used. A consistently low fibre volume ratio and a perfect impregnation of the fibre enable the production of efficient fibre reinforced components. For the controlled, non-porous cure of the components autoclaves are used. We're happy to meet your individual requirements and can deliver the required fibres an the necessary profile on short notice.
| Prepregs | |||||
|---|---|---|---|---|---|
| Art. No. | Name | Curing | Application | Data Sheet | |
| Time/°C | TG | Download | |||
| HACOPREG LTP180 |
Low temperature prepreg | 23h@45°C 8h@60°C 4h@70°C |
185- 190°C |
mould building in the field of automotive, aircraft and wind energy industries |  |
| HACOPREG MTP125 |
Middle temperature prepreg | 12h@80°C 1h@120°C 15min.@140°C |
125- 130°C |
high breaking strength for application in the field of automotive, nautical and sporting industries | |
| HACOPREG MTP130 |
Middle temperature prepreg |
12h@60°C 45min.@120°C 15min.@140°C |
125- 130°C |
high breaking strength for application in the field of automotive, nautical and sporting industries | |
| HACOPREG MTP140 |
Middle temperature prepreg |
12h@80°C 60min.@125°C 60min.@130°C |
140- 145°C |
good mechanical properties, high temperature resistance for application in the field of automotive, nautical and sporting industries | |
| HACOPREG MTP160 |
Middle temperature prepreg |
12h@80°C 60min.@120°C 60min.@150°C |
good mechanical properties, high temperature resistance for application in the field of automotive, nautical and sporting industries | |
|
The prepregs are manufactured in combination with our standard fabric types according to the customers' request. For possible material combinations please refer to the attached pdf-document. Combinations with other fabric types are available upon request. Should you not find the required material for your purpose, don't hesitate to contact us. We'll develop a tailor made solution for you!